In this article, the role of surface sites of modified zeolites with semiconductor nanoparticles as alternative photocatalyts for protecting post-harvest foodstuff from the detrimental effects of ethylene is addressed. Two single and one double catalyst based on zinc and copper oxides supported over modified zeolite samples were prepared. Physical, chemical, and surface properties of prepared materials were studied by several characterization methods. UV-Vis absorption spectra show that the applied modification procedures increase the optical absorption of light in the UV and visible regions, suggesting that an increase in the photocatalytic activity could take place mainly in the obtained co-impregnated catalyst. An ethylene conversion around 50% was achieved when the parent natural zeolite support was modified with both transition metal oxides, obtaining higher removal efficiency in comparison to single oxide catalysts. Adsorption and photocatalytic oxidation experiments were also performed using single and double catalysts supported over fumed silica, attaining lower ethylene conversion and thus highlighting the role of zeolite surfaces as adsorption sites for ethylene during photocatalytic reactions. Operando diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) studies reveal that a synergistic mechanism occurs, involving ethylene adsorption at acidic sites of zeolite and its photocatalytic oxidation due to the generation of radicals by the light activation of nanoparticles of zinc and copper oxides.

The influence of surface physical-chemical characteristics of Chilean natural zeolite on the catalytic ozonation of toluene is presented in this article. Surface characteristics of natural zeolite were modified by acid treatment with hydrochloric acid and ion-exchange with ammonium sulphate. Prior to catalytic ozonation assays, natural and chemically modified zeolite samples were thermally treated at 623 and 823 K in order to enhance Brønsted and Lewis acid sites formation, respectively. NaturalandmodifiedzeolitesampleswerecharacterisedbyN2 adsorptionat77K,elementalanalysis, X-ray fluorescence, and Fourier transform infrared (FTIR) spectroscopy, using pyridine as a probe molecule. The highest values of the reaction rate of toluene oxidation were observed when NH4Z1 and 2NH4Z1 zeolite samples were used. Those samples registered the highest density values of Lewis acid sites compared to other samples used here. Results indicate that the presence of strong Lewis acid sites at the 2NH4Z1 zeolite surface causes an increase in the reaction rate of toluene oxidation, confirming the role of Lewis acid sites during the catalytic ozonation of toluene at room temperature. Lewis acid sites decompose gaseous ozone into atomic oxygen, which reacts with the adsorbed toluene at Brønsted acid sites. On the other hand, no significant contribution of Brønsted acid sites on the reaction rate was registered when NH4Z1 and 2NH4Z1 zeolite samples were used.